TRIBOTECHNICAL CHARACTERISTICS OF ELECTROSPARK COATINGS FORMED USING NON-CONTACT TECHNOLOGYI
Keywords:
coating, plasma, morphology, friction, titaniumAbstract
The article examines the tribological characteristics of electrospark coatings (ESCs) formed using non-contact technology. This technological approach makes it possible to reduce the defectiveness of coatings formed by ESA, as well as to obtain antifriction layers from non-conducting materials, in particular from oxide ceramics. Coatings of various origins obtained on titanium substrates were studied. It has been established that the formation of multicomponent and multifunctional electrospark coatings during the interaction of low-voltage discharge plasma with powder materials makes it possible to obtain protective layers with high antifriction properties, ensuring a reduction in the friction coefficient by 30-35% and wear rate by 1.5-2 times compared to the original material VT1 -0.
References
Структура и адгезионные характеристики электроискровых покрытий, получаемых по бесконтактной технологии / В. В. Михайлов [и др.] // Современные методы и технологии создания и обработки материалов. В 3 кн. Кн. 1. Материаловедение: сб. науч. тр. – Минск: ФТИ НАН Беларуси, 2023. – С. 206-213.
Е. В. Овчинников // Порошковая металлургия: инженерия поверхности, новые порошковые композиционные материалы. Сварка. В 2 ч. Ч. 2: сб. докладов 13-го Междунар. симпозиума, Минск, 5-7 апр. 2023 г. – Минск: Беларуская навука, 2023. – С. 255-260
ГОСТ Р 57558-2017 «Аддитивные технологические процессы. Базовые принципы» - С.12.
P. D. Enriquea, A.Keshavarzkermania, R.Esmaeilizadeha, S. Peterkin, H. Jahed, E. Toyserkania, N. Y. Zhou Enhancing fatigue life of additive manufactured parts with electrospark deposition post-processing Additive Manufacturing -2020-V.36 – p.1-13.
Kazak, N.N.; Mikhaylov, V.V.; Chekan, N.M.; Ovchinnikov, Y.V.; Eysymont, Y.I.; Kovsh, A.A. Korrozionnaya stoykost’ i prochnostnyye kharakteristiki nanostrukturirovannykh pokrytiy, poluchennykh metodom elektroiskrovogo legiro-vaniya. In Proceedings of the International Conference Actual Strength Issues, Vitebsk, Belarus, 25–29 May 2020; pp. 320–322 [ISBN 978-985-6967-44-6.]
Овчинников Е. В., Михайлов В. В., Чекан Н. М. Технология синтеза наноструктур при электроискровом легировании в книге: Актуальные проблемы прочности. Монография. Под редакцией В. В. Рубаника. Молодечно, 2020. С. 345-358.
Овчинников Е.В. Физико-механические характеристики нанокомпозиционных покрытий, формируемых методом электроискрового легирования/ В.В. Михайлов [ и др.] // Веснік ГрДУ імя Янкі Купалы. Сер. Сер 6, Тэхніка. - 2019.- Т.9.- № 2.- С.45-53
Katinas, E.; Jankauskas, V.; Kazak, N.; Mikhailov, V. Improving Abrasive Wear Resistance for Steel Hardox 400 by Electro-Spark Deposition. / J. Frict. Wear -2019. – V. 40 – p.100–106, [ISSN 1068-3666].