PECULIARITIES OF SURFACE ALLOYING OF HARDOX 600 STEEL USING A FIBER LASER
Keywords:
laser alloying, surface layer, microstructure, microhardnessAbstract
The features of surface alloying of Hardox 600 steel using b4c, WC, and Ni powders based on exposure to ytterbium fiber laser radiation are studied. At a radiation power of ~ 2 kW, high-quality doping zones can be observed more stably over the entire range of laser beam scanning speeds under study. With an increase in the depth of the alloying zone when using b4c, the microhardness decreases, which is associated with a decrease in the concentration of introduced alloying elements. The microhardness of the layer can vary in the range of 7300 - 16000 MPa.
References
Астапчик С. А., Голубев В. С., Новикова О. В., Процкевич Л. И., Чеботько И. С. Лазерное легирование сталей с использованием порошковых материалов./ Весцi АН БССР, сер. фiзiка-тэхнiчных навук. – 1989, №4. – С.7-13.
Григорьянц, А. Г. Технологические процессы лазерной обработки / А. Г. Григорьянц, И. Н. Шиганов, А. И. Мисюров ; под ред. А. Г. Григорьянца. – М.: МГТУ им. Н. Э. Баумана, 2006. – 664 с.
Астапчик, С. А. Лазерные технологии в машиностроении и металлообработке / В. С. Голубев, А. Г. Маклаков. – Минск: Белорусская наука, 2008. – 252 с.
Астапчик, С. А. Лазерные технологии: возможности и перспективы обработки деталей и инструмента / C. А. Астапчик, В. С. Голубев, А. Г. Маклаков // Тяжелое машиностроение. – 2004, № 2. – С. 33–37.
Девойно, О. Г. Технология формирования износостойких поверхностей лазерным легированием / O. Г. Девойно. – Минск: Технопринт, 2001. – 180 с.
Бернацкий, А. В. Лазерное поверхностное легирование стальных изделий (Обзор) / А. В. Бернацкий //Автоматическая сварка. – 2013, №. 12. – С. 3 – 10.
В. С. Голубев, И. И. Вегера, О. Чернашеюс, В. В. Чаевский. Лазерная обработка материалов с изменением химического состава поверхностного слоя. / Вестник БарГУ, сер.Технические науки – 2019,Т.7. – С.34-42